Sodium silicate, also known as water glass or liquid glass, available in liquid and solid (prill) form, is a compound used in cements, passive fire protection, refractories, textile and lumber processing.

Properties

Sodium carbonate and silicon dioxide react when molten to form sodium silicate and carbon dioxide.

Sodium silicate is a white solid that is soluble in water, producing an alkaline solution. There are many kinds of this compound, including sodium orthosilicate, Na₄SiO₄; sodium metasilicate, Na₂SiO₃; sodium polysilicate, (Na₂SiO₃)n; sodium pyrosilicate, Na₆Si₂O₇, and others. All are glassy, colourless and dissolve in water.

Sodium silicate is stable in neutral and alkaline solutions. In acidic solutions, the silicate ion reacts with hydrogen ions to form silicic acid, which when heated and roasted forms silica gel, a hard, glassy substance that absorbs water readily.

Metal repair

Sodium silicate is used, along with magnesium silicate, in muffler repair paste. When dissolved in water, both sodium silicate, and magnesium silicate form a thick paste that is easy to apply. When the exhaust system of an internal combustion engine heats up to its operating temperature, the heat drives out all of the excess water from the paste. The Silicate compounds that are left over have glass-like properties, making a somewhat permanent, brittle repair.

Automotive Repair

Sodium silicate can be used in older automobiles to seal leaks in the cooling system. A jar of "liquid glass" is poured into the radiator and allowed to circulate. Minute holes and gaps are sealed, often curing radiator leaks and faulty cylinder-head gaskets. This approach is often used by disreputable used-car salespersons.

Food preservation

Sodium silicate was also used as an egg preservation agent in the early 20th Century with large success. When fresh eggs are immersed in it, bacteria which cause the eggs to spoil are kept out and water is kept in. Eggs can be kept fresh using this method for up to nine months. When boiling eggs preserved this way, it is well advised to pin-prick the egg to allow steam to escape because the shell is no longer porous.

Timber Treatment

The use of sodium silicate as a timber treatment for pressure-treated wood actually began some time in the 19th century. It is suggested as an alternative for using silicate of potash (Potassium silicate), but that it is more expensive in a book called "Handy Farm Devices and How to Make Them" by Rolfe Cobleigh, published in 1910. Since 1998 scientists have researched methods for rendering sodium silicate insoluable once the lumber has been treated with it. With or without the additonal process, treating wood with Sodium Silicate preserves wood from insects and possesses some flame-retardant properties.

Concrete and General Masonry Treatment

Concrete treated with a Sodium Silicate solution helps to significantly reduce porosity in most masonry products such as concrete, stucco, plasters. A chemical reaction occurs with the excess CaOH in the concrete that permanently binds the silicates with the surface making them far more wearable and water repellent. It is generally advised to apply only after initial cure has taken place (7 days or so depending on conditions).

Passive Fire Protection

Sodium silicates are inherently intumescent. They come in prill (solid beads) form, as well as the liquid, water glass. The solid sheet form (Palusol) must be waterproofed to ensure longterm functionality. Standard, solid, bead form sodium silicates have been used as aggregate within silicone rubber to manufacture plastic pipe firestop devices. The silicone rubber was insufficient waterproofing to preserve the intumescing function and the products had to be recalled, which is problematic for firestops that are concealed behing drywall in buildings. Pastes for caulking purposes are likewise unstable even for very short periods of time. This too has resulted in recalls and even litigation. Only 3M's "Expantrol" version, which has an external heat treatment that helps to seal the outer surface, as part of its process standard, has achieved sufficient longevity to qualify for DIBt ^* approvals for use in firestopping. Not unlike other intumescents, sodium silicate, both in bead form and in liquid form are inherently endothermic, due to liquid water in the water glass and hydrates in the prill form. The absence of mandatory ageing tests, whereby PFP system are made to undergo system performance tests after the ageing and humidity exposures are at the root of the continued availability in North America in PFP products that can become inoperable within weeks of installation. Indiscriminate use of sodium silicates without proper waterproofing measures are contributors to the malaise. When sodium silicates are adequately protected, they function extremely well and reliably over long periods of time. Evidence of this can be seen in the many DIBt approvals for plastic pipe firestop devices using Palusol, which use waterproofed sodium silicate sheets.

Refractory Use

Water glass is a useful binder of solids, such as vermiculite and perlite. When blended with the aforementioned lightweight aggregates, water glass can be used to make hard, high-temperature insulation boards used for refractories, passive fire protection and high temperature insulations, such as moulded pipe insulation applications. When mixed with finely divided mineral powders, such as vermiculite dust (which is common scrap from the exfoliation process), one can produce high temperature adhesives. The intumescence disappears in the presence of finely divided mineral dust, whereby the waterglass becomes a mere matrix. Waterglass is inexpensive and abundantly available, which makes its use popular in many applications, especially refractories.

External links

• PQ CORP: Sodium Silicate Product Line
• International Chemical Safety Card 1137

See also

• Intumescent
• Endothermic
• Passive fire protection
• Firestop
• Fireproofing

Sodium compounds | Silicates | Fire

Alkalisilikate | ケイ酸ナトリウム