Dyneema® is a synthetic fiber based on ultra high molecular weight polyethylene, 15 times stronger than steel and up to 40% stronger than Kevlar®. It is usually used in bulletproof vests, bow strings, climbing equipment, fishing line and high performance sails in yachting. Dyneema® was invented by DSM in 1979. It has been in commercial production since 1990 at a plant in Heerlen, the Netherlands. In the Far East, DSM has a cooperation agreement with Toyobo Co. for commercial production in Japan. In the United States, DSM has granted a license to Honeywell, which had developed a chemically identical product on its own. The Honeywell product is sold under the brand name Spectra®. Though the production details will undoubtedly be different, the resulting materials are comparable. This article refers to both materials by the name Dyneema®. Dyneema® is a registered trademark of Royal DSM N.V. (The Netherlands).
Chemistry and properties
For details, see the properties section of Ultra high molecular weight polyethylene.
Dyneema® fibers derive their strength from the extreme length of each individual molecule. The fibre can attain a parallel orientation greater than 95% and a level of crystallinity of up to 85%. In contrast, Kevlar® derives its strength from strong bonding between relatively short molecules.
Its melting point is around 144 or 152 degrees Celsius, and according to DSM, it is not advisable to use Dyneema® at temperatures exceeding 80 to 100 °C for long periods of time. It becomes brittle at temperatures below –150 °C. This contrasts strongly with other high-performance fibers, which tend to be quite heat-resistant.
The fibers feel slippery, similar to polypropylene and other hydrophobic fibers. Most people do not like the way Dyneema® feels; for this reason, it is not often used in fabric. The slipperiness also makes such fibers less suitable for use in fibre reinforced plastics.
Another problem, in some applications, is that Dyneema® will creep, meaning it will deform when placed under any long term stress. Like other olefins, it is very resistant to water, moisture, most chemicals, UV radiation, and micro-organisms.
Production
Dyneema® fibers are made using a DSM patented (1979) method called gel spinning. A precisely heated gel of UHMWPE is processed by an extruder through a spinneret. The extrudate is drawn through the air and then cooled in a water bath. The end result is a fiber with a high degree of molecular orientation, and therefore exceptional tensile strength.
Applications
For body armor, the fibers are generally aligned and bonded into sheets, which are then layered at various angles to give the resulting composite material strength in all directions.
Both Spectra® and Dyneema® excel as fishing line as they have less stretch, are more abrasion resistant, and are thinner than traditional monofilament line.
In recent years certain items of climbing equipment have started making use of Dyneema®. In particular "slings", sewn loops of material that can be wrapped around sections of rock, hitched (tied) to other pieces of equipment or even tied directly to a tensioned line using a special prussik knot, have benefited from this material. It has limited applications however as items made from this material do not stretch and therefore a fall on them involves considerable shock loading of the other pieces of equipment and the climber's body. They are however much lighter and finer than the alternatives (nylon) and therefore are very popular. Usually sold in lengths of 10, 30, 60, 120, or 400 cm at either 8, 10 or 12 mm width, these slings have a breaking strength of around 22 kN.
High-performance ropes for sailing and parasailing are made of Dyneema® as well.
Recently developed additions to the US Military's Interceptor body armor, designed to offer arm and leg protection, are said to utilize a form of Dyneema® fabric.
It is also used in snowboards, often in combination with carbon fiber, reinforcing the fiberglass composite material, adding stiffness and improving its flex characteristics.
Dyneema® is the preferred material for sport kite lines for two main reasons. First the low stretch means that control inputs to the kite are transferred quickly and secondly the low friction allows the kite to remain controllable up to about ten twists in the line.